Mechanical Properties as a Function of Zinc Content, Degree of Cold Drawing and Annealing Temperature in α-Brasses

Abstract
Increasing zinc content up to 28 wt.% zinc was found to increase stress level and ductility.Degrees of cold drawing up to 99% reduction in cross sectional area increase stress level while decrease ductility for the different Cu-Zn alloys studied.Annealing after cold drawing increases ductility but decreases stress level.Abrupt decrease in ductility was observed after high temperature annealing of ...
View PDF
Keywords
Annealing (glass)
Zinc
Degree (music)
Materials science
Metallurgy
Physics
Acoustics


pdf file

Mechanical Properties as a Function of Zinc Content, Degree of Cold Drawing and Annealing Temperature in α-Brasses
pdf file

Mechanical Properties as a Function of Zinc Content, Degree of Cold Drawing and Annealing Temperature in α-Brasses

Abstract
Increasing zinc content up to 28 wt.% zinc was found to increase stress level and ductility.Degrees of cold drawing up to 99% reduction in cross sectional area increase stress level while decrease ductility for the different Cu-Zn alloys studied.Annealing after cold drawing increases ductility but decreases stress level.Abrupt decrease in ductility was observed after high temperature annealing of ...
View PDF
Keywords
Annealing (glass)
Zinc
Degree (music)
Materials science
Metallurgy
Physics
Acoustics


pdf file